Damaging inner materials when stripping any layer of the cable, is a ticking time-bomb. A fiber which has been scratched on the outer diameter may indeed function perfectly well for some time.
Stress points from which cracks in the glass can propagate over time, lead to (potentially) sudden and catastrophic failure of the cable assembly. This is why most Cable Assembly Houses will implement some method of evaluating newly-stripped fibers to help ensure no unseen damage has been done during the stripping process. A common such method is to perform a 45-degree bend test on the fiber where, if the fiber OD had been “nicked” by the stripping tool, this bend would cause the fiber to break at the scratch point. While this would then require re-stripping of the cable, it’s a much better problem to resolve than a fiber break in a deployed product!
Additional resources from the FOC team include:
- Glossary, Acronyms, Military Specifications for Connectors: http://bit.ly/2a2EFn8
- Q&A Resource: email technical questions to AskFOC@focenter.com
Have questions about this FOC Tip?
Contact FOC with questions at: (800) 473-4237 / 508-992-6464 or email: FiberOpticCenter@focenter.com and we will respond ASAP.
- Considerations regarding freezing epoxy – THAWING - November 13, 2019
- Crystallization in Epoxies: How to Identify and Reverse it - October 23, 2019
- Measuring Insertion Loss and Return Loss Recommendations to Achieve the Best and Most Accurate Test Measurement - October 23, 2019
- Cross-Sectioning Fiber Optic Connectors: An Effective Diagnostic Method to Identify Defects and Resolve Process Issues - October 23, 2019
- The “Ideal” Fiber Height for a Fiber Optic Connector – and How to Achieve It - October 23, 2019
- Considerations regarding freezing epoxy – recommended length of time - October 23, 2019
- Techniques when using stripping tools - October 18, 2019
- Considerations regarding freezing epoxy – implementing process controls - September 18, 2019
- Aramid yarns and Good stripping techniques - September 11, 2019
- When the “back-side” connector end-face is contaminated, it is difficult to have access to remove the connector for cleaning - September 8, 2019