ÅngströmLap® Aluminum Oxide Lapping Film Disc - 8 inch 0.5µm (micron)
AO05F803N100
AngstromLap 0.5um Aluminum Oxide Lapping Film, 8" Disc with 3mil Backing, package of 100 discs.
ÅngströmLap Aluminum Oxide Lapping Film is recommended when diamond lapping film is not needed, like in many fiber optic multimode applications. Some aluminum oxides can even be used as the final polish. The 0.5µm and 0.3µm will produce return losses of -50 dB or better, but because they cut the glass at a much quicker rate than the ceramic, undercut may occur. The lapping film disc is used for applications in fiber optic connector polishing, flat lapping, superfinishing and media head finishing.
Aluminum Oxide 0.5µm lapping film is typically used as a final film for MM connectors. To achieve the best finish with 0.5um AlOx, FOC recommends using it with Ultra Polish Solution. When used with the Ultra Polish Solution, it will give a near flawless finish.
The 8" film disc is the standard size for the Ultra Tec Ultrapol 1200, some Buelher polishing machine, as well as others.
Lapping Film Features:
Aluminum Oxide 0.5µm lapping film is typically used as a final film for MM connectors. To achieve the best finish with 0.5um AlOx, FOC recommends using it with Ultra Polish Solution. When used with the Ultra Polish Solution, it will give a near flawless finish.
The 8" film disc is the standard size for the Ultra Tec Ultrapol 1200, some Buelher polishing machine, as well as others.
Lapping Film Features:
- Film Color: White
- Tape Total Thickness: 86.0 ± 2.0 µm
- Surface Roughness: 0.18 ± 0.04 µm
- Particle Type: Aluminum Oxide film
- Grit Size: 0.5 micron (0.5µm)
- Base Film Material: Polyethylene terephthalate
- Base Film Thickness: 3 mil (75 µm)
- Quantity: 100 discs
- Process Parameters Type: CF
- Non-PSA Backed Film
- Product Life: Guaranteed up to 5 years from the manufactured date