EPO-TEK® HYB-353ND-TX2 High Temperature Epoxy, Hybrid Heat & UV Cure - Pre-Mixed and Frozen 3cc Syringe (5-Pack Sample)

The EPO-TEK^® HYB-353ND-TX2 UV Hybrid Epoxy is a single-component, high-temperature hybrid epoxy designed for semiconductor, fiber optic, and medical applications. It offers cured performance similar to EPO-TEK 353ND, but is modified for initial UV (ultraviolet)  tacking and features higher thixotropy than HYB-353ND. Available in a 5-pack of premixed and frozen syringes (3 cc automatic dispensing syringes).

Recommended Cure: UV tack at 100 mW/cm² for 10 seconds @ 240–365 nm, followed by a 150°C (302°F), 30-minute thermal cure.

Features of HYB-353ND-TX2:

• Supports active alignment of lenses, diodes, and optical components
• UV (ultraviolet) tacking for precise positioning
• Paste-like viscosity
• Pot life: < 2 Days

Applications:

• Fiber Optics: Fiber bonding and component alignment
• Optoelectronics: Optical sub-assemblies; lens, diode, and component bonding
• Piezoelectric bonding
• LiDAR and IR Sensors

Physical Properties:

• Consistency: Pourable paste
• Viscosity (23°C) @ 10 rpm: 17,000-35,000 cPs
• Thixotropic Index: 1.7
• Glass Transition Temperature, Tg: ≥ 90°C (≥ 194°F)
• Shore D Hardness: 80
• Coefficient of Thermal Expansion (CTE):
  • Below Tg: 63 x 10^-6 in/in°C
  • Above Tg: 179 x 10^-6 in/in°C
• Suggested Operating Temperature: < 350 °C (Intermittent); < 662°F
• Particle Size: ≤ 20 microns

Optical Properties @ 23°C:

• Spectral Transmission:
  • ≥ 50% @ 550 nm
  • ≥ 95% @ 1,100-1,600 nm
  • ≥ 98% @ 800-1,000 nm
• Refractive Index: 1.5457 @ 589 nm

See Datasheet for additional properties and application notes