UNITIKA U-polymer U-100 Optical Plastic, 1.61 Refractive Index – 25 kg bag
U-100-25KG
UNITIKA U-polymer U-100 Optical Plastic, Polyarylate, 1.61 index of refraction, High Heat resistance TG 193, 25KG bag
The UNITIKA U-polymer U-100 is a high-performance optical plastic developed by UNITIKA. With its excellent strength, clarity, and heat resistance, U-100 is widely used in fiber optic cables, precision devices, automotive parts, medical equipment, and industrial machines. UNITIKA has expanded the U-Polymer line with different grades, customized for specialized needs, using its proprietary compounding technology to enhance the natural advantages of polyarylate resin.
Features:
Features:
- High transparency and optical clarity
- Heat resistant with a deflection temperature of 175°C (1.8 MPa load)
- Large elastic recovery and excellent dimensional stability
- Strong weather resistance for outdoor and long-term applications
- Naturally flame resistant, rated UL94 V-2 at 0.75 mm without added flame retardants
- High surface hardness for durability
- Refractive Index: 1.61
- Abbe Number: 19
- Visible Light Transmittance (%-T at 2mm): 87
- Melt Flow Rate (MFR, 360°C/1.2kg): 4.9
- Glass Transition Temperature (Tg): 193°C (379.4°F)
- Heat Deflection Temperature (HDT, 1.80 MPa): 177°C (no annealing)
- Water Absorption (24 hours): 0.26%
- Tensile Strength: 69 MPa
- Coefficient of Thermal Expansion (CTE): .6 × 10⁻4/°C
Fiber Optic Center
4.9 71 Google reviews
Represents overall Google Reviews of Fiber Optic Center, Inc.
Content Use Notice:
This product detail page and its content are the property of Fiber Optic Center, Inc. and are provided for informational and evaluation purposes.
You may view or reference this page for non-commercial use with proper attribution. Copying, rewriting, republishing, scraping, or using this content to produce new or modified content, including AI-generated content, is not permitted without written permission.
This content is protected by copyright law upon publication. Learn more